On 11 November 2019, one of the two PW100 series engines of a Bombardier DHC8-300 failed catastrophically when takeoff power was set prior to brake release. The Investigation found that the power turbine shaft had fractured in two places and all first and second stage power turbine blades had separated from their disks. The shaft failure was found to have been caused by fatigue cracking initiated by corrosion pitting which was assessed as probably the result of prolonged marine low-altitude operations by the aircraft. It was found that this fatigue cracking could increase undetected during service between scheduled inspections.